please contact us for mass production schedule. specifcations in this bulletin are subject to change without notice. nippon chemi-con corporation 1698 1 hxa series high reliability and high voltage are realized by hybrid electrolyte endurance with ripple current : 4,000 hours at 125 rated voltage range : 16 to 80v dc , capacitance range : 10 to 470f for high temperature and high reliability applications. (automotive equipment, base station equipment, etc.) specifications items characteristics category temperature range -55 to +125 rated voltage range 16 to 80v dc capacitance tolerance 20% m (at 20 , 120hz) leakage current i=0.01cv where, i : max. leakage current (a), c : nominal capacitance (f), v : rated voltage (v) (at 20 after 2 minutes) dissipation factor (tan ) rated voltage (v dc ) 16v 25v 35v 50v 63v 80v (at 20 , 120hz) tan (max.) 0.16 0.14 0.12 0.10 0.08 0.08 low temperature characteristics (max. impedance ratio) z(-25 ) / z(+20 ) Q 1.5 z(-55 ) / z(+20 ) Q 2.0 (at 100khz) endurance the following specifcations shall be satisfed when the capacitors are restored to 20 after subjected to dc voltage with the rated ripple current is applied (the peak voltage shall not exceed the rated voltage) for 4,000 hours at 125 . capacitance change Q 30 of the initial value d.f. (tan ) Q 200 of the initial specifed value esr Q 200 of the initial specifed value leakage current Q the initial specifed value shelf life the following specifcations shall be satisfed when the capacitors are restored to 20 after exposing them for 1,000 hours at 125 without voltage applied. before the measurement, the capacitor shall be preconditioned by applying voltage according to item 4.1 of jis c 5101-4. capacitance change Q 30 of the initial value d.f. (tan ) Q 200 of the initial specifed value esr Q 200 of the initial specifed value leakage current Q the initial specifed value part numbering system 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 h h x a a r a m g supplement code size code capacitance tolerance code capacitance code (ex. 47f:470, 100f:101) taping code terminal code voltage code (ex. 35v:350) series code category size code d l a b c w p f61 6.3 5.8 6.6 6.6 7.2 0.5 to 0.8 1.9 f80 6.3 7.7 6.6 6.6 7.2 0.5 to 0.8 1.9 ha0 8 10.0 8.3 8.3 9.0 0.7 to 1.1 3.1 ja0 10 10.0 10.3 10.3 11.0 0.7 to 1.1 4.5 marking ex) 35v47f 26a 47 v ha ? rated voltage symbol rated voltage (v dc ) symbol 16 c 25 e 35 v 50 h 63 j 80 k vent for ja0 dimensions mm terminal code : a note : l0.5 for ha0 and ja0 d0.5 0.3max. l0.3(note) b0.2 c0.2 p ? a0.2 w engineering bulletin introductory no.830i/may.2014 conductive polymer hybrid aluminum electrolytic capacitors
please contact us for mass production schedule. specifcations in this bulletin are subject to change without notice. nippon chemi-con corporation 1698 2 pma series npcap tm - standard ratings recommended solder land(based on the px series) [mm] reflow profile location of capacitor c a b b solder land on pc board 217 230 peak preheat peak temperature time (sec.) max. period of time over 230 temperature on the top of capacitor temperature of capacitor terminal and ( ) max. period of time over 217 recommended reflow soldering conditions nippon chemi-con corporation 1595 engineering bulletin conductive polymer aluminum solid capacitors no.824c / oct.2012 tentative 2 cap (f) rated ripple current -55 Q tx Q +85 * 1 +85 < tx Q +105 * 1 ( marms/100khz) part no. 16 20 25 apma160ara680mf40s 40 f40 apma160ara151mf60s 18 f60 apma160ara390mf40s 2,200 3,300 2,200 2,700 4,100 2,700 40 f40 apma200ara470mf40s 45 f40 apma200ara151mf60s 20 f60 apma160ara221mf60s 2,100 3,200 3,300 2,600 3,700 4,100 18 f60 apma250ara220mf40s 50 f40 apma250ara560mf60s 26 f60 apma250ara150mf40s 2,000 2,800 2,000 2,400 3,400 2,400 50 544 1,200 312 470 1,500 1,760 275 700 187 f40 68 150 39 47 150 220 22 56 15 wv (v dc ) size code leakage current (amax/after 2min.) esr (m max/ 2 0 , 100k to 300khz) speci?cations in this bulletin are subject to change without notice. please ask us for technical specifications before purchase and use. *1 tx: ambient temperature voltage range(v dc ) reflow number preheat time maintained above 230 peak temp. 16 to 25v 1-cycle only 150 to 180 120 sec.max. 50 sec.max. 250 max. 30 sec.max. 40 sec.max. 2-cycle allowed time maintained above 217 40 sec.max. size code a b c f40,f60 1.6 3.5 1.9 hxa series standard ratings wv (v dc ) cap (f) size code esr (mmax/20 , 100khz) rated ripple current (marms/125 , 100khz) part no. 16 82 f61 45 950 hhxa160ara820mf61g 150 f80 27 1,300 hhxa160ara151mf80g 270 ha0 22 1,700 hhxa160ara271mha0g 470 ja0 18 2,100 hhxa160ara471mja0g 25 56 f61 50 900 hhxa250ara560mf61g 100 f80 30 1,400 hhxa250ara101mf80g 220 ha0 27 1,600 hhxa250ara221mha0g 330 ja0 20 2,000 hhxa250ara331mja0g 35 47 f61 60 900 hhxa350ara470mf61g 68 f80 35 1,400 hhxa350ara680mf80g 150 ha0 27 1,600 hhxa350ara151mha0g 270 ja0 20 2,000 hhxa350ara271mja0g 50 22 f61 80 750 hhxa500ara220mf61g 33 f80 40 1,100 hhxa500ara330mf80g 68 ha0 30 1,250 HHXA500ARA680MHA0G 100 ja0 28 1,600 hhxa500ara101mja0g 63 10 f61 120 700 hhxa630ara100mf61g 22 f80 80 900 hhxa630ara220mf80g 33 ha0 40 1,100 hhxa630ara330mha0g 56 ja0 30 1,400 hhxa630ara560mja0g 80 22 ha0 45 1,100 hhxa800ara220mha0g 39 ja0 35 1,200 hhxa800ara390mja0g recommended reflow soldering conditions the following conditions are recommended for air convection and infrared refow soldering on the smd products on to a glass epoxy circuit boards by cream solder. the dimensions of the glass epoxy boards with resist are 90500.8mm. the temperatures shown are the surface temperature values on the top of the can and on the capacitor terminals. refow should be performed twice or less. please ensure that the capacitor became cold enough to the room temperature (5 to 35 ) before the second refow. refow profle size code preheat time maintained above 217 time maintained above 230 peak temp. refow number f61, f80 150 to 180 120 sec. max. 50 sec. max. 40 sec. max. 260 max. 2-cycle allowed ha0, ja0 50 sec. max. 40 sec. max. 260 max. 1-cycle only 245 max. 2-cycle allowed engineering bulletin introductory no.830i/may.2014 conductive polymer hybrid aluminum electrolytic capacitors
|
